Effects of in situ cross-linked graphene oxide-containing gelatin methacrylate anhydride hydrogel on wound vascularization of full-thickness skin defect in mice

Objective To prepare graphene oxide (GO)-containing gelatin methacrylate anhydride (GelMA) hydrogel and to investigate the effects of in situ photopolymerized GO-GelMA composite hydrogel in wound vascularization of full-thickness skin defect in mice.

Methods The experimental study method was used. The 50 μL of 0.2 mg/mL GO solution was evenly applied onto the conductive gel, and the structure and size of GO were observed under field emission scanning electron microscope after drying. Human skin fibroblasts (HSFs) were divided into 0 μg/mL GO (without GO solution, the same as below) group, 0.1 μg/mL GO group, 1.0 μg/mL GO group, 5.0 μg/mL GO group, and 10.0 μg/mL GO group treated with GO of the corresponding final mass concentration, and the absorbance value was detected using a microplate analyzer after 48 h of culture to reflect the proliferation activity of cells (n=6). HSFs and human umbilical vein vascular endothelial cells (HUVECs) were divided into 0 μg/mL GO group, 0.1 μg/mL GO group, 1.0 μg/mL GO group, and 5.0 μg/mL GO group treated with GO of the corresponding final mass concentration, and the migration rates of HSFs at 24 and 36 h after scratching (n=5) and HUVECs at 12 h after scratching (n=3) were detected by scratch test, and the level of vascular endothelial growth factor (VEGF) secreted by HSFs after 4, 6, and 8 h of culture was detected by enzyme-linked immunosorbent assay method (n=3). The prepared GO-GelMA composite hydrogels containing GO of the corresponding final mass concentration were set as 0 μg/mL GO composite hydrogel group, 0.1 μg/mL GO composite hydrogel group, 1.0 μg/mL GO composite hydrogel group, and 5.0 μg/mL GO composite hydrogel group to observe their properties before and after cross-linking, and to detect the release of GO after soaking with phosphate buffer solution for 3 and 7 d (n=3). The full-thickness skin defect wounds were made on the back of 16 6-week-old female C57BL/6 mice. The mice treated with in situ cross-linked GO-GelMA composite hydrogel containing GO of the corresponding final mass concentration were divided into 0 μg/mL GO composite hydrogel group, 0.1 μg/mL GO composite hydrogel group, 1.0 μg/mL GO composite hydrogel group, and 5.0 μg/mL GO composite hydrogel group according to the random number table, with 4 mice in each group. The general condition of wound was observed and the wound healing rate was calculated on 3, 7, and 14 d of treatment, the wound blood perfusion was detected by laser Doppler flowmetry on 3, 7, and 14 d of treatment and the mean perfusion unit (MPU) ratio was calculated, and the wound vascularization on 7 d of treatment was observed after hematoxylin-eosin staining and the vascular density was calculated (n=3). The wound tissue of mice in 0 μg/mL GO composite hydrogel group and 0.1 μg/mL GO composite hydrogel group on 7 d of treatment was collected to observe the relationship between the distribution of GO and neovascularization by hematoxylin-eosin staining (n=3) and the expression of VEGF by immunohistochemical staining. Data were statistically analyzed with analysis of variance for repeated measurement, one-way analysis of variance, and Tukey's method.

Results GO had a multilayered lamellar structure with the width of about 20 μm and the length of about 50 μm. The absorbance value of HSFs in 10.0 μg/mL GO group was significantly lower than that in 0 μg/mL GO group after 48 h of culture (q=7.64, P<0.01). At 24 h after scratching, the migration rates of HSFs were similar in the four groups (P>0.05); at 36 h after scratching, the migration rate of HSFs in 0.1 μg/mL GO group was significantly higher than that in 0 μg/mL GO group, 1.0 μg/mL GO group, and 5.0 μg/mL GO group (with q values of 7.48, 10.81, and 10.20, respectively, P<0.01). At 12 h after scratching, the migration rate of HUVECs in 0.1 μg/mL GO group was significantly higher than that in 0 μg/mL GO group, 1.0 μg/mL GO group, and 5.0 μg/mL GO group (with q values of 7.11, 8.99, and 14.92, respectively, P<0.01), and the migration rate of HUVECs in 5.0 μg/mL GO group was significantly lower than that in 0 μg/mL GO group and 1.0 μg/mL GO group (with q values of 7.81 and 5.33, respectively, P<0.05 or P<0.01 ). At 4 and 6 h of culture, the VEGF expressions of HSFs in the four groups were similar (P>0.05); at 8 h of culture, the VEGF expression of HSFs in 0.1 μg/mL GO group was significantly higher than that in 0 μg/mL GO group and 5.0 μg/mL GO group (with q values of 4.75 and 4.48, respectively, P<0.05). The GO-GelMA composite hydrogels in the four groups were all red liquid before cross-linking, which turned to light yellow gel after cross-linking, with no significant difference in fluidity. The GO in the GO-GelMA composite hydrogel of 0 μg/mL GO composite hydrogel group had no release of GO at all time points; the GO in the GO-GelMA composite hydrogels of the other 3 groups was partially released on 3 d of soaking, and all the GO was released on 7 d of soaking. From 3 to 14 d of treatment, the wounds of mice in the 4 groups were covered with hydrogel dressings, kept moist, and gradually healed. On 3, 7, and 14 d of treatment, the wound healing rates of mice in the four groups were similar (P>0.05). On 3 d of treatment, the MPU ratio of wound of mice in 0.1 μg/mL GO composite hydrogel group was significantly higher than that in 0 μg/mL GO composite hydrogel group, 1.0 μg/mL GO composite hydrogel group, and 5.0 μg/mL GO composite hydrogel group (with q values of 10.70, 11.83, and 10.65, respectively, P<0.05 or P<0.01). On 7 and 14 d of treatment, the MPU ratios of wound of mice in the four groups were similar (P>0.05). The MPU ratio of wound of mice in 0.1 μg/mL GO composite hydrogel group on 7 d of treatment was significantly lower than that on 3 d of treatment (q=14.38, P<0.05), and that on 14 d of treatment was significantly lower than that on 7 d of treatment (q=27.78, P<0.01). On 7 d of treatment, the neovascular density of wound of mice on 7 d of treatment was 120.7±4.1 per 200 times of visual field, which was significantly higher than 61.7±1.3, 77.7±10.2, and 99.0±7.9 per 200 times of visual field in 0 μg/mL GO composite hydrogel group, 1.0 μg/mL GO composite hydrogel group, and 5.0 μg/mL GO composite hydrogel group (with q values of 12.88, 7.79, and 6.70, respectively, P<0.01), and the neovascular density of wound of mice in 1.0 μg/mL GO composite hydrogel group and 5.0 μg/mL GO composite hydrogel group was significantly higher than that in 0 μg/mL GO composite hydrogel group (with q values of 5.10 and 6.19, respectively, P<0.05). On 7 d of treatment, cluster of new blood vessels in wound of mice in 0.1 μg/mL GO composite hydrogel group was significantly more than that in 0 μg/mL GO composite hydrogel group, and the new blood vessels were clustered near the GO; a large amount of VEGF was expressed in wound of mice in 0.1 μg/mL GO composite hydrogel group in the distribution area of GO and new blood vessels.

Conclusions GO with mass concentration lower than 10.0 μg/mL had no adverse effect on proliferation activity of HSFs, and GO of 0.1 μg/mL can promote the migration of HSFs and HUVECs, and can promote the secretion of VEGF in HSFs. In situ photopolymerized of GO-GelMA composite hydrogel dressing can promote the wound neovascularization of full-thickness skin defect in mice and increase wound blood perfusion in the early stage, with GO showing an enrichment effect on angiogenesis, and the mechanism may be related to the role of GO in promoting the secretion of VEGF by wound cells.