Adsorptive denitrification of NaY molecular sieve modified by Cr³⁺

HONG Xin,
TANG Ke^,

More Information

Corresponding author: Tel: 86-416-4198019, E-mail: tangke0001@163.com

摘要

摘要: 对Cr³⁺离子改性NaY分子筛的实验条件进行了研究, 通过XRD、FT-IR、N₂吸附-脱附等方法对改性后的CrY分子筛进行表征, 确定最佳改性条件为温度40℃, Cr³⁺浓度0.5 mol/L, 改性两次。FT-IR谱图表明, CrY分子筛波数1 147 cm^-1处峰明显消失, 且波数1 024 cm^-1峰与标准的NaY分子筛相比发生了蓝移现象, 可以判定Cr³⁺交换到分子筛骨架上。考察了吸附时间和温度对CrY分子筛吸附脱除模拟燃料中喹啉的影响。结果表明, 吸附温度对吸附影响不大, 可在室温下进行。CrY对喹啉的吸附主要为化学吸附, 且吸附类型为配位吸附和π络合吸附, 最佳吸附时间为30 min, 吸附等温线线性回归表明, CrY分子筛对喹啉吸附动力学模型为L型和F型混合吸附。
- NaY分子筛 /
- 改性 /
- 吸附脱氮 /
- Cr³⁺离子
Abstract: The modification of NaY by chromium ion was systemically studied.The modified CrY molecular sieve was characterized by X-ray diffraction (XRD), Fourier transform infrared spectrum (FT-IR) and nitrogen adsorption.The experimental results show that the optimum condition of modification are two times modification with 0.5 mol/L Cr³⁺at 40℃.The result of FT-IR suggested the peak disappeared at 1 147 cm^-1 and the peak generated a blue shift at 1 024 cm^-1, indicating that Cr³⁺ had exchanged Na⁺ in the framework of NaY molecular sieve.Static adsorption denitrification of a model fuel on CrY molecular sieve had carried out at different adsorption time and temperature.The results showed that the adsorption of quinoline on CrY molecular sieve was chemical adsorption and the adsorption type was coordination adsorption and π complex adsorption.The adsorption effect was better at room temperature for 30 min.The adsorption of quinoline over CrY molecular sieve belongs to Langmuir adsorption and Freundlich adsorption model.
- NaY molecular sieve /
- modification /
- adsorptive denitrification /
- chromium ion

HTML全文

图 1 不同温度下Cr³⁺改性的NaY分子筛的XRD谱图

Figure 1. XRD spectra of NaY modified by Cr³⁺ at different temperature

下载: 全尺寸图片幻灯片

图 2 不同Cr³⁺改性次数的NaY分子筛XRD谱图

Figure 2. XRD spectra of NaY modified by Cr³⁺ with different times

下载: 全尺寸图片幻灯片

图 3 不同Cr³⁺浓度改性NaY分子筛的XRD谱图

Figure 3. XRD spectra of NaY modified by different Cr³⁺concentrations

下载: 全尺寸图片幻灯片

图 4 CrY分子筛的吸附-脱附曲线及H-K孔径分布曲线

Figure 4. Adsorption isotherm and H-K pore size distribution of CrY

下载: 全尺寸图片幻灯片

图 5 改性后CrY分子筛和标准NaY分子筛红外光谱谱图

Figure 5. FT-IR spectra of CrY and NaY molecular sieve

下载: 全尺寸图片幻灯片

图 6 吸附时间对NaY及CrY吸附脱除模拟燃料中碱氮的影响

Figure 6. Effect of adsorption time on adsorption denitrification in model fuel of NaY and CrY

■: NaY adsorption capacity; ▼: CrY adsorption capacity; □: NaY removal rate; ▽: CrY removal rate

下载: 全尺寸图片幻灯片

图 7 吸附温度对CrY吸附脱除模拟燃料中碱氮的影响

Figure 7. Effect of adsorption temperature on adsorption denitrification in model fuel of CrY

下载: 全尺寸图片幻灯片

图 8 CrY吸附模拟燃料中喹啉的吸附等温线

Figure 8. Adsorption isotherm for CrY adsorption quinoline from model fuel

下载: 全尺寸图片幻灯片

图 9 吸附等温线L型和F型线性拟合曲线

Figure 9. Linear fitting of the Langmuir and Freundlich adsorption isotherm

下载: 全尺寸图片幻灯片

参考文献(22)

[1]	DHEER S, ANJU C, MITRA B P, AMARJIT S S.A comparative evaluation of nitrogen compounds in petroleum distillates[J].Chromatographia, 2011, 74(1/2):121-126.
[2]	吕志凤, 战风涛, 李林, 苏贻勋.催化裂化柴油中氮化物的分析[J].石油化工, 2001, 30(5):399-401. http://www.cnki.com.cn/Article/CJFDTOTAL-SYHG200105014.htm LV Zhi-feng, ZHAN Feng-tao, LI Lin, SU Yi-xun.Separation and identification of nitrogen compounds in diesels[J].Petrochem Technol, 2001, 30(5):399-401. http://www.cnki.com.cn/Article/CJFDTOTAL-SYHG200105014.htm
[3]	BELTRAMONE A R, CROSSLEY S, RESASCO D E, ALVAREZ W E, CHOUDHARY T V.Inhibition of the hydrogenation and hydrodesulfurization reactions by nitrogen compounds over NiMo/Al₂O₃[J].Catal Lett, 2008, 123(1/2):181-185.
[4]	LIU K, FLORA T T.Effect of the nitrogen heterocyclic compounds on hydrodesulfurization using in situ hydrogen and a dispersed Mo catalysi[J].Catal Today, 2010, 149(1/2):28-34.
[5]	HANAFL S A, MOHAMED M S.Recent trends in the cleaning of diesel fuels via desulfurization processes[J].Energy Source Part A, 2011, 33(6):495-511. doi: 10.1080/15567030903058360
[6]	SANO Y, CHOI K H, KORAI Y.Effects of nitrogen and refractory sulfur species removal on the deep HDS of gas oil[J].Appl Catal B:Environ, 2004, 53(3):169-174. doi: 10.1016/j.apcatb.2004.05.014
[7]	RABARIHOELA-RAKOTOVAO V, DIEHL F, BRUNET S.Compounds on the transformation of the refractory 4, 6-Dimethyldibenzothiophene over a NiMoP/Al₂O₃ catalyst[J].Catal Lett, 2009, 129:50-60. doi: 10.1007/s10562-008-9777-x
[8]	JVRGEN B, JVRGEN K.Andreas Weigel Olaf Schröder, Thomas Brüning, Michael Müller Ernst Hallier, G tz Westphal.Influence of fuel properties, nitrogen oxides, and exhaust treatment by an oxidation catalytic converter on the mutagenicity of diesel engine emissions[J].Arch Toxicol, 2006, 80(8):540-546. doi: 10.1007/s00204-006-0088-y
[9]	刘兴利, 王榕, 李永红.吸附法脱除烷基化用汽油中的碱性氮化物[J].离子交换与吸附, 2009, 25(1):45-51. http://www.cnki.com.cn/Article/CJFDTOTAL-LJYX200901008.htm LIU Xing-li, WANG Rong, LI Yong-hong.Denitrogenation of FCC denitrogenation of FCC gasoline used as the feedstock of alkylation by several different adsorbents[J].Ion Exc Adsorpt, 2009, 25(1):45-51. http://www.cnki.com.cn/Article/CJFDTOTAL-LJYX200901008.htm
[10]	陈月株, 孙玉华, 周亚松.石油馏分中脱除氮化物的方法:中国, CN 1045459C[P].1999-10-06. CHEN Yue-zhu, SUN Yu-hua, ZHOU Ya-song.Method of removing nitrogen compounds in petroleum fractions:CN, CN 1045459C[P].1999-10-06.
[11]	朱金柱, 沈健.SBA-15吸附脱除油品中的碱性氮化物[J].石油学报 (石油加工), 2012, 40(11):566-570. ZHU Jin-zhu, SHEN Jian.Adsorption of basic nitrogen compounds from oil by SBA-15 zeolite[J].Acta Pet Sin (Pet Process Sect), 2012, 40(11):566-570.
[12]	LAREDO G C, VEGA-MERINO P M, TREJO-ZÁRRAGA F, CASTILLO J.Denitrogenation of middle distillates using adsorbent materials towards ULSD production:A review[J].Fuel Process Technol, 2013, 106:21-32. doi: 10.1016/j.fuproc.2012.09.057
[13]	徐晓宇, 孙悦, 沈健, 翟玉龙.HY和USY分子筛对模拟油品中碱性氮化物的吸附行为[J].化工进展, 2014, 33(4):1035-1040. http://www.cnki.com.cn/Article/CJFDTOTAL-HGJZ201404052.htm XU Xiao-yu, SUN Yue, SHEN Jian, ZHAI Yu-long.Adsorption behavior of basic nitrides in model oil on HY and USY molecular sieves[J].Chem Ind Eng Prog, 2014, 33(4):1035-1040. http://www.cnki.com.cn/Article/CJFDTOTAL-HGJZ201404052.htm
[14]	翟玉龙, 沈健.HY分子筛吸附脱除油品中碱性氮化物的研究[J].石油炼制与化工, 2011, 42(1):41-44. http://www.cnki.com.cn/Article/CJFDTOTAL-SYLH201101017.htm ZHAI Yu-long, SHEN Jian.Study on the adsorption of basic nitrogen compounds from oil with HY molecular sieve[J].Pet Process Petrochem, 2011, 42(1):41-44. http://www.cnki.com.cn/Article/CJFDTOTAL-SYLH201101017.htm
[15]	王福帅, 李会鹏, 赵华, 房斌斌.NaY/β复合分子筛改性及对模拟柴油中氮化物的吸附性能[J].石油炼制与化工, 2012, 43(11):59-62. http://www.cnki.com.cn/Article/CJFDTOTAL-SYLH201211016.htm WANG Fu-shuai, LI Hui-peng, ZHAO Hua, FANG Bin-bin.Modification of NaY/β composite molecular sieve and its adsorption performance of removing nitrogen containing compounds in model oil[J].Pet Process Petrochem, 2012, 43(11):59-62. http://www.cnki.com.cn/Article/CJFDTOTAL-SYLH201211016.htm
[16]	唐磊, 沈健.改性Y型分子筛吸附脱除油品中碱性氮化物的研究[J].应用化工, 2014, 43(6):1078-1085. http://www.cnki.com.cn/Article/CJFDTOTAL-SXHG201406030.htm TANG Lei, SHEN Jian.Study on adsorpting basic nitrogen compounds from oil with the modified Y zeolite[J].Appl Chem Ind, 2014, 43(6):1078-1085. http://www.cnki.com.cn/Article/CJFDTOTAL-SXHG201406030.htm
[17]	洪新, 唐克.NaY分子筛的改性及吸附脱氮性能[J].燃料化学学报, 2015, 43(2):214-220. http://rlhxxb.sxicc.ac.cn/CN/abstract/abstract18577.shtml HONG Xin, TANG Ke.Modification and adsorptive denitrification of NaY molecular sieve[J].J Fuel Chem Technol, 2015, 43(2):214-220. http://rlhxxb.sxicc.ac.cn/CN/abstract/abstract18577.shtml
[18]	ZHANG H, SONG H Y.Study of adsorptive denitrogenation of diesel fuel over mesoporous molecular sieves based on breakthrough curves[J].Ind Eng Chem Res, 2012, 51:16059-16065. doi: 10.1021/ie302169r
[19]	迟志明.介孔分子筛用于柴油吸附脱氮的基础研究[D].北京:中国石油大学, 2010. CHI Zhi-ming.Basic research of Al-MCM-41 molecular sieve for denitrogenation of diese oil[D].Beijing:China University of Petroleum, 2010.
[20]	张晗.燃料中含氮化合物的吸附脱除[D].大连:大连理工大学, 2009. ZHANG Han.Adsorptive removal of nitrogen-containing compounds from fuel[D].Dalian:Dalian University of Technology, 2009.
[21]	洪新, 唐克.杂原子介孔Co-MCM-41分子筛的制备及其吸附脱氮性能[J].燃料化学学报, 2015, 43(6):720-727. http://rlhxxb.sxicc.ac.cn/CN/abstract/abstract18646.shtml HONG Xin, TANG Ke.Preparation and deep adsorption denitrification from diesel oil of heteroatoms mesoporous molecular sieve Co-MCM-41[J].J Fuel Chem Technol, 2015, 43(6):720-727. http://rlhxxb.sxicc.ac.cn/CN/abstract/abstract18646.shtml
[22]	罗勤慧, 沈孟长, 丁益.Cr³⁺的水解聚合作用的研究[J].化学学报, 1982, 40(2):125-132. LUO Qin-hui, SHEN Meng-chang, DING Yi.Studies on the hydrolytic polymerization of Cr³⁺ Ⅰ[J].Acta Chim Sin, 1982, 40(2):125-132.